Specification
Data printout: with bluetooth printer
Main test parameter: HV
Convertible parameters: HRA, HRB, HRC, HBW, HS, MPa
Measurement range: 50~1599HV, 20~68HRC, 85~650HB, 41~100HRB
61~85.6HRA, 34.2~97.3HS, 255~2180MPa
Resolution: 1HV, 0.1HRA, 0.1HRB, 0.1HRC, 1HB, 0.1HS, 1MPa
Accuracy: ±4%HV, ±4%HB, ±1.5HR
Calibration method:
Normal material: one-point calibration
Special materials: multi-point calibration
Operating temperature: -10°C ~ 40°C
Power supply: built-in rechargeable lithium battery (for 10 hours working)
Dimension of main unit: 190×82×30mm
Dimension of probe: 150xØ22mm
Weight: 540g
Standard delivery
Main unit: 1pc
19.6N manual probe: 1pc
Bluetooth printer: 1pc
charger: 1pc
USB cable: 1pc
Randomized standard hardness block: 1pc
- Small size, light weight, portable, convenient for on-line measurement and can be used to measure large workpieces
- Support 360°measurement, fast test speed, the fastest results in 1 second
- Standard Vickers indentation, small test indentation and low damage to the workpiece
- 100 measurement data sets and 10 calibration data sets can be stored
- Large display, directly shows the current measured value, maximum value, minimum value, average value and unit conversion value
- For unspecified conversion tables and unknown materials, multi-point calibration on any hardness scale you can choose to eliminate of systematic errors due to conversion tables
- According to DIN 50159, ASTM A1038 standards
Applications:
1. Hardness measurement of flange edges and gearoot stampings, gears and gear grooves with hardened die sheet surfaces, taper sections
2. Hardness measurement of shafts and thin-walled pipes and vessels
3. Hardness measurement of thin plated layers, wheels, turbine rotors and welded parts
4. Measurement of the depth of a certain hole diameter deep holes, curvature of the larger dents and convex marks, irregular planes
5. Covering the majority of hardness measurement of industrial production of ferrous metals, non-ferrous metals and their alloys